    您所在的位置:網站首頁 > > 產品中心 > XLPE絕緣材料 > 化學交聯絕緣料化學交聯聚乙烯絕緣料 XEJ-10 XEJ-35
    化學交聯聚乙烯絕緣料 XEJ-10 XEJ-35
    Chemical Cross-Linkable PE Insulation Compound...
    型號:0

    參考價:¥

    說明:如您對該產品感興趣,請在此輸入您的手機號將本產品的地址 發送至您手機上。

    Product description產品描述
    Chemical cross-linkable PE insulation compound for power cables which regards advanced LDPE resin as the main raw material, adds antioxidant, cross-linking agent and other accessory ingredients, is manufactured by advanced closed extruding equipment. It has excellent extrusion property and physical property, its impurity content is controlled within limits. This product is mainly used as the insulation of medium-low voltage cross-linking cables. Long-term working temperature is 90℃.
    電力電纜用可化學交聯聚乙烯絕緣料是以優質低密度聚乙烯樹脂為主要原材料,加入抗氧劑、交聯劑等助劑,采用先進的封閉式混煉裝置加工而成,它兼有良好的擠出性能和物理性能,雜質含量符合要求,專用于生產中、低壓交聯電線電纜,長期工作溫度為90℃。
     
     
    Processing Indicator 加工工藝
    Recommend to process with the PE extruder
    建議使用聚乙烯專用擠出機進行加工。


    Model
    牌號
    Machine Barrel Temperature
    機筒溫度
    Molding Temprature
    機頭溫度
    XEJ-10/ XEJ-35 100-115℃ 110-115℃
     
     
     
    Physical and Electrical Properties 物理和電氣性能

    Item

    試驗項目

    Unit
    單位

    Standard Data

    標準值

    XEJ-10 XEJ-35
    Density
    密度
    g/cm3 0.922±0.003 0.922±0.003
    Tensile Strength
    拉伸強度
    MPa ≥13.5 ≥13.5
    Elongation at Break
    斷裂伸長率
    % ≥350 ≥350
    Brittle Temperature with Low Temperature
    低溫脆化溫度
    -76 -76
    20℃Volume Resistivity
    20℃體積電阻率
    Ω·m ≥1.0×1014 ≥1.0×1014
    20℃Dielectric Strength,50Hz
    20℃介電強度, 50Hz
    MV/m ≥25.0 ≥25.0
    20℃Dielectric Constant,50Hz
    20℃介電常數, 50Hz
    --- ≤2.35 ≤2.35
    20℃Dielectric Dissipation Factor,50Hz
    20℃介質損耗因數, 50Hz
    --- ≤0.001 ≤0.0005
    Impurity Content(Per 1.0Kg)
    雜質含量(每1.0Kg)
    0.175-0.250 mm
    ≥0.250 mm
     
     
    個(No.)
    個(No.)
    ---  
     
    ≤5
    0
    Air Aging Condition
    熱空氣老化條件
    135℃×168h
    Tensile Strength Variation After Aging
    拉伸強度變化率
    % ≤±20 ≤±20
    Elongation Variation After Aging
    斷裂伸長變化率
    % ≤±20 ≤±20
    Hot Set Test Condition
    熱延伸試驗條件
    200℃×0.2MPa×15min
    Hot Elongation
    負荷下伸長率
    % ≤80 ≤80