    您所在的位置:網站首頁 > > 產品中心 > XLPE絕緣材料 > 化學交聯絕緣料10KV及以下化學交聯黑色聚乙烯架空絕緣料 YJW-10
    10KV及以下化學交聯黑色聚乙烯架空絕緣料 YJW-10
    Chemical Cross-Linkable PE Overhead Insulation Black Compound (≤10KV) ...
    型號:0

    參考價:¥

    說明:如您對該產品感興趣,請在此輸入您的手機號將本產品的地址 發送至您手機上。

    Product description 產品描述
    Chemical cross-linkable PE insulation black compound for power cables which regard advanced LDPE resin as the main material, add antioxidant, cross-linking agent and other accessory additives, is manufactured by advanced closed extruder. It has excellent extrusion property and physical property, impurity content is controlled within limits. This product is mainly used for the insulation of medium-low voltage cross-linking overhead cables. Working temperature is 90℃.It is applicable for 10KV and below cross-linking cables.
    電力電纜用黑色可化學交聯聚乙烯絕緣料是以優質低密度聚乙烯樹脂為主要原材料,加入抗氧劑、交聯劑等配合劑,采用先進的封閉式混煉裝置加工而成,它兼有良好的擠出性能和物理性能,雜質含量符合要求,專用于生產中、低壓交聯架空電纜絕緣,長期工作溫度為90℃,本產品適用于10KV及以下交聯電線電纜。
     
    Processing Indicator 加工工藝
    Recommend to process with the PE extruder. 建議使用聚乙烯專用擠出機進行加工。


    Model
    牌號
    Machine Barrel Temperature
    機筒溫度
    Molding Temperature
    機頭溫度
    YJW-10 100-115℃ 110-115℃

    Physical and Electrical Properties 物理和電氣性能
    Item
    試驗項目
    Unit
    單位
    Technical requirements
    技術要求
    Tensile Strength
    拉伸強度
    MPa ≥13.0
    Elongation at Break
    斷裂伸長率
    % ≥300
    Brittle Temperature with Low Temperature
    低溫脆化溫度
    -76
    20℃Volume Resistivity
    20℃體積電阻率
    Ω·m ≥1.0×1013
    20℃Dielectric Strength,50Hz
    20℃介電強度, 50Hz
    MV/m ≥22.0
    20℃Dielectric Dissipation Factor,50Hz
    20℃介質損耗因數, 50Hz
    --- ≤0.001
    Resistance to Environmental Stress Cracking F0
    耐環境應力開裂F0
    h ≥1000
    Air Aging Condition
    熱空氣老化條件
    135℃×168h
    Tensile Strength Variation After Aging
    拉伸強度變化率
    % ±20
    Elongation Variation After Aging
    斷裂伸長變化率
    % ±20
    Artificial Weathering Aging
    人工氣候老化0-1008h
    Tensile Strength Variation After Aging
    拉伸強度變化率
    % ±30
    Elongation Variation After Aging
    斷裂伸長率變化率
    % ±30
    Artificial Weathering Aging
    人工氣候老化504-1008h
    Tensile Strength Variation After Aging
    拉伸強度變化率
    % ±30
    Elongation Variation After Aging
    斷裂伸長率變化率
    % ±30
    Hot Set Test Condition
    熱延伸試驗條件
    200℃×0.2MPa×15min
    Hot Elongation
    負荷下伸長率
    % ≤80
    Permanent Deformation After Cooling
    冷卻后永久形變
    % ≤5