    環保型105℃汽車原線料 W-0596, W-0597, W-0598
    105℃Lead-free Automotive Wire Compound...
    型號:0

    參考價:¥

    說明:如您對該產品感興趣,請在此輸入您的手機號將本產品的地址 發送至您手機上。
    Product Description 產品描述
    105℃lead-free automotive wire compound is granular compound which is manufactured through mixing, plasticizing and pelletizing processes. It regards advanced PVC resin as the basic raw materials, and adds plasticizer, stabilizer and other accessory ingredients. This product has excellent mechanical and physical properties, electrical property and good processability. It can meet RoHS Standard. The cables with it can meet LV112, VW60306, DIN72551 and other related standards. The highest working temperature is 105℃.
    環保型105℃汽車原線料是以優質聚氯乙烯樹脂為基料,加入特種增塑劑、穩定劑等助劑,經混合、塑化、造粒而成的粒狀電纜料。產品具有良好的機械物理性能和電性能,加工性能優異,符合RoHS環保標準。制成電線后可以滿足LV 112、VW 60306、DIN 72551等相關標準,最高工作溫度為105℃。
     
    Product Details  產品明細
    Model
    牌號
    Application
    用途
    W-0596 >16mm2cables
    16mm2以上規格的電線
    W-0597 0.5mm2 ~6mm2 cables
    0.5mm2 ~6mm2及以規格的電線
    W-0598 ≤ 0.5mm2 cables
    0.5mm2及以下規格的電線
     
     
    Processing Indicator 加工工藝
    Recommend to use of single-screw extruders with L/D= 20-25.
    建議使用普通長徑比為20-25的單螺桿擠出機進行生產。
    Model
    牌號
    Machine Barrel Temperature
    機筒溫度
    Molding Temperature
    機頭溫度
    W-0596 / W-0597 165-185℃ 180-190℃
    W-0598 165-185℃ 185-190℃
     
     
    Physical and Electrical Properties 機械物理性能及電性能指標

    Item

    試驗項目

    Unit
    單位
    Molding Temperature
    技術要求
    W-0596 W-0597 W-0598
    Density
    比重
    \ 1.32±0.02 1.32±0.02 1.32±0.02
    Tensile Strength
    拉伸強度
    MPa ≥18.0 ≥18.0 ≥18.0
    Elongation at Break
    斷裂伸長率
    % ≥250 ≥250 ≥250
    200℃Thermal Stability
    200℃時熱穩定時間
    min ≥200 ≥200 ≥200
    20℃Volume Resistivity
    20℃時體積電阻率
    Ω.m ≥1×1011 ≥1×1011 ≥1×1011
    Dielectric Strength
    介電強度
    MV/m ≥22 ≥20 ≥20
    Brittle Temperature with Impact
    沖擊脆化溫度
    -25 -25 -25
    Hardness
    硬度
    Shore A 88±2 94±2 97±2
    Thermal Aging
    熱老化試驗
    \ 136℃×168h
    Tensile Strength Variation
    拉伸強度變化率
    % ±20 ±20 ±20
    Elongation Variation
    斷裂伸長率變化率
    % ±20 ±20 ±20